Influence of aluminum phosphate on the tribocorrosion performance of chemically bonded phosphate ceramic coatings

In this study, chemically bonded phosphate ceramic coatings (CBPCCs) with different contents of aluminum phosphate (AP) are prepared on stainless steel (AISI 304L). Differential scanning calorimetry, X-ray diffraction, contact angle test, and a tribocorrosion experiment are carried out to clarify the role of AP in the tribocorrosion performance of CBPCCs. The results show that, with the increase in the AP content, the enthalpy of curing increases because of the greater formation of the bonding phase AlPO₄. Both in static corrosion and in tribocorrosion, the corrosion current density of CBPCCs achieves the lowest value when the weight ratio of AP to polytetrafluoroethylene is about 0.78. Additionally, the influence mechanism of AP on tribocorrosion is clarified. AlPO₄ from the reaction between AP and Al₂O₃ has excellent mechanical properties and can enhance the wear resistance of CBPCCs by reducing the mechanical wear and the increased wear due to corrosion. The alumina particles wrapped by AlPO₄ can form a dense and smooth surface and change the direction of electrolyte propagation, which leads to the increase in the tribocorrosion resistance of CBPCCs.     

氮含量及固溶温度对21-6-9奥氏体不锈钢组织和硬度的影响

为了探讨氮含量及固溶温度对21-6-9不锈钢组织和硬度的影响,分别在950、1000、1050和1100 ℃对3种不同氮含量的热轧态21-6-9不锈钢进行1 h固溶处理,通过光学显微镜观察其组织结构,结合Thermo-Calc热力学计算对试验钢的微观组织进行分析,并对其进行硬度测试。结果表明,0.20%~0.28%N的21-6-9不锈钢热轧后沿轧制方向析出铁素体,且钢中铁素体经950~1100 ℃固溶处理可消除,当N含量达到0.34%时,试验钢中不再出现铁素体。随着固溶处理温度的升高,21-6-9不锈钢的晶粒组织长大,硬度降低。N含量的增加可显著提高固溶态21-6-9不锈钢的硬度,其增加程度随固溶处理温度的升高而减弱。     

Localized corrosion of (lean) duplex stainless steels in immersion units of urban wastewater treatment plants

With lower alloying cost and higher mechanical properties, lean duplex stainless steels can be an alternative to the more commonly used austenitic stainless steels. However, these alloys are still not the preferred choice, probably due to a lack of field experience. A study was thus initiated in view of defining the limits of use of selected (lean) duplexes for urban wastewater treatment units. The present paper shows the localized corrosion performance of selected lean duplexes in chloride contaminated solutions. The results are compared with austenitic S30403 and S31603 and with the more standard duplexes S82441 and S32205. The effect of welding was also investigated. Exposures in field municipal wastewater plants were conducted for 1 year in low and high chloride content units. The results show that lean duplexes S32101 and S32202 can be used as alternatives to S30403 and S31603 in low chloride electrolytes. At 500 ppm of chloride content, duplex stainless steel S32304 showed better corrosion resistance than S30403 and S31603. For higher chloride contents (1000 ppm and above) the standard duplexes S82441 and S32205 shall be preferred.     

Depassivation and repassivation of stainless steels by stepwise pH change

Immersion tests with different stainless steels have been performed, while the pH was stepwise decreased and then increased again. During 8.5-day exposure, the depassivation and repassivation pH values as a function of pitting resistance equivalent number were determined. There is always a gap between both pH values (depassivation and repassivation), indicating that for every steel, there are conditions where an existing passive layer can be maintained but cannot be rebuilt after depassivation. In such environments, the passive layer is thicker, consisting mainly of molybdenum and iron rich oxides, while chromium is dissolved. Usually, depending on conditions, the passive layer is more chromium-rich, especially the inner layer. This is relevant, for example, for acidizing jobs in oil and gas industry, proving that repassivation after acidizing will happen promptly, when the pH is increased again.     

30Cr13不锈钢冶炼过程夹杂物控制技术

  针对30Cr13生产过程中存在的轧材非金属夹杂物合格率偏低仅85%左右的问题，通过对30Cr13不锈钢精炼过程钢中非金属夹杂物存在形态进行分析，并结合现有精炼工艺制度，在实验室研究的基础上制定了不锈钢精炼过程非金属夹杂物控制方案。工业应用后，精炼结束钢中大于5 μm的非金属夹杂物总数、形状以及尺寸等参数均得到了有效改善，钢水洁净度大大提高。     

304不锈钢不同精炼渣碱度下夹杂物的演变

 为了提高304不锈钢的产品质量，结合生产实际，利用热力学计算和扫描电镜能谱分析方法, 研究了硅脱氧条件下，LF精炼渣碱度对304不锈钢在LF精炼、连铸过程夹杂物变化规律的影响。试验结果表明,随着冶炼过程进行，全氧质量分数和夹杂物数量依次减小。304不锈钢采用1.75高碱度炉渣，可以得到较低的全氧质量分数和夹杂物数量，但是夹杂物中Al2O3质量分数高，夹杂物熔点高。采用1.53低碱度炉渣，钢液中全氧质量分数较采用高碱度炉渣高，但是夹杂物中CaO、Al2O3质量分数相对较低，SiO2和MnO质量分数较高，夹杂物熔点低。针对304不锈钢产品可以采用不同的生产工艺路线来满足产品的不同需求。